{"id":2374,"date":"2026-06-24T10:15:03","date_gmt":"2026-06-24T02:15:03","guid":{"rendered":"https:\/\/jeez-semicon.com\/?p=2374"},"modified":"2026-06-24T10:15:03","modified_gmt":"2026-06-24T02:15:03","slug":"cmp-process-steps-how-chemical-mechanical-planarization-works-2","status":"publish","type":"post","link":"https:\/\/jeez-semicon.com\/ja\/blog\/cmp-process-steps-how-chemical-mechanical-planarization-works-2\/","title":{"rendered":"CMP Process Steps: How Chemical Mechanical Planarization Works"},"content":{"rendered":"<!-- JEEZ | Cluster 02 | CMP Process Steps: How Chemical Mechanical Planarization Works -->\n<link rel=\"preconnect\" href=\"https:\/\/fonts.googleapis.com\">\n<link rel=\"preconnect\" href=\"https:\/\/fonts.gstatic.com\" crossorigin>\n<link href=\"https:\/\/fonts.googleapis.com\/css2?family=Syne:wght@600;700;800&#038;family=Inter:ital,wght@0,400;0,500;0,600;1,400&#038;display=swap\" rel=\"stylesheet\">\n<style>\n.jeez-pl*,.jeez-pl*::before,.jeez-pl*::after{box-sizing:border-box}\n.jeez-pl{--jz-navy:#0B1D3A;--jz-navy-mid:#0D2B4E;--jz-teal:#0D9488;--jz-teal-dark:#0A7A70;--jz-teal-xlight:#F0FDFB;--jz-blue:#1D6FA4;--jz-blue-lite:#EFF8FF;--jz-text:#1E293B;--jz-muted:#64748B;--jz-border:#E2E8F0;--jz-bg:#F8FAFC;--jz-gold:#B45309;--jz-gold-lite:#FFFBEB;--jz-white:#FFFFFF;--jz-radius:10px;font-family:'Inter',system-ui,sans-serif;font-size:16px;line-height:1.78;color:var(--jz-text);max-width:880px;margin:0 auto;padding:0 16px 60px}\n.jeez-pl .jz-hero{background:linear-gradient(140deg,#0B1D3A 0%,#0D2B4E 55%,#0F3A60 100%);border-radius:16px;padding:52px 48px 44px;margin-bottom:40px;position:relative;overflow:hidden}\n.jeez-pl .jz-hero::before{content:'';position:absolute;inset:0;background:repeating-linear-gradient(0deg,transparent 0px,transparent 39px,rgba(13,148,136,.07) 39px,rgba(13,148,136,.07) 40px);pointer-events:none}\n.jeez-pl .jz-hero-eyebrow{display:inline-flex;align-items:center;gap:6px;background:rgba(13,148,136,.18);color:#5EEAD4;font-size:11px;font-weight:700;letter-spacing:.1em;text-transform:uppercase;padding:4px 14px;border-radius:99px;border:1px solid rgba(94,234,212,.28);margin-bottom:20px;position:relative;z-index:1}\n.jeez-pl .jz-hero h1{font-family:'Syne',sans-serif;font-size:clamp(1.55rem,3.5vw,2.35rem);font-weight:800;color:#fff;line-height:1.18;margin:0 0 20px;position:relative;z-index:1;max-width:700px}\n.jeez-pl .jz-hero-lead{color:rgba(255,255,255,.77);font-size:1.04rem;line-height:1.76;max-width:660px;margin:0 0 26px;position:relative;z-index:1}\n.jeez-pl .jz-hero-meta{display:flex;flex-wrap:wrap;align-items:center;gap:6px 14px;font-size:12px;color:rgba(255,255,255,.5);position:relative;z-index:1}\n.jeez-pl .jz-hero-meta .jz-pipe{color:rgba(255,255,255,.25)}\n.jeez-pl .jz-hero-meta strong{color:#5EEAD4;font-weight:600}\n.jeez-pl .jz-back-link{display:inline-flex;align-items:center;gap:6px;font-size:12.5px;font-weight:600;color:var(--jz-muted);text-decoration:none;margin-bottom:18px;padding:5px 14px;border:1px solid var(--jz-border);border-radius:99px;background:var(--jz-bg);transition:color .15s}\n.jeez-pl .jz-back-link:hover{color:var(--jz-teal);text-decoration:none;border-color:rgba(13,148,136,.4)}\n.jeez-pl .jz-toc{background:var(--jz-bg);border:1px solid var(--jz-border);border-left:4px solid var(--jz-teal);border-radius:var(--jz-radius);padding:26px 30px 22px;margin-bottom:46px}\n.jeez-pl .jz-toc-label{font-size:11px;font-weight:700;letter-spacing:.1em;text-transform:uppercase;color:var(--jz-teal);margin-bottom:14px;display:block}\n.jeez-pl .jz-toc ol{margin:0;padding-left:18px;columns:2;column-gap:28px}\n.jeez-pl .jz-toc li{margin-bottom:8px;font-size:13.5px;break-inside:avoid;line-height:1.4}\n.jeez-pl .jz-toc a{color:var(--jz-blue);text-decoration:none;font-weight:500}\n.jeez-pl .jz-toc a:hover{color:var(--jz-teal)}\n.jeez-pl section{margin-bottom:52px}\n.jeez-pl h2{font-family:'Syne',sans-serif;font-size:1.52rem;font-weight:800;color:var(--jz-navy);margin:0 0 18px;padding-bottom:13px;border-bottom:2px solid var(--jz-border);line-height:1.25;scroll-margin-top:24px}\n.jeez-pl h2 .jz-sn{color:var(--jz-teal);font-size:.88rem;margin-right:8px;font-weight:700}\n.jeez-pl h3{font-family:'Syne',sans-serif;font-size:1.1rem;font-weight:700;color:var(--jz-navy);margin:30px 0 10px;line-height:1.35}\n.jeez-pl h4{font-family:'Inter',sans-serif;font-size:.95rem;font-weight:600;color:var(--jz-navy);margin:16px 0 6px}\n.jeez-pl p{margin:0 0 16px}\n.jeez-pl p:last-child{margin-bottom:0}\n.jeez-pl a{color:var(--jz-teal);font-weight:500;text-decoration:none}\n.jeez-pl a:hover{color:var(--jz-teal-dark);text-decoration:underline}\n.jeez-pl ul,.jeez-pl ol{margin:10px 0 16px;padding-left:22px}\n.jeez-pl li{margin-bottom:7px}\n.jeez-pl ul li::marker{color:var(--jz-teal)}\n.jeez-pl .jz-callout{border-left:4px solid var(--jz-teal);background:var(--jz-teal-xlight);border-radius:0 var(--jz-radius) var(--jz-radius) 0;padding:16px 20px;margin:20px 0}\n.jeez-pl .jz-callout.blue{border-left-color:var(--jz-blue);background:var(--jz-blue-lite)}\n.jeez-pl .jz-callout.gold{border-left-color:var(--jz-gold);background:var(--jz-gold-lite)}\n.jeez-pl .jz-callout-tag{font-size:10px;font-weight:700;letter-spacing:.1em;text-transform:uppercase;color:var(--jz-teal);display:block;margin-bottom:6px}\n.jeez-pl .jz-callout.blue .jz-callout-tag{color:var(--jz-blue)}\n.jeez-pl .jz-callout.gold .jz-callout-tag{color:var(--jz-gold)}\n.jeez-pl .jz-table-wrap{overflow-x:auto;margin:22px 0;border-radius:var(--jz-radius);border:1px solid var(--jz-border);box-shadow:0 1px 4px rgba(0,0,0,.05)}\n.jeez-pl .jz-table-wrap table{width:100%;border-collapse:collapse;font-size:13px;line-height:1.5}\n.jeez-pl .jz-table-wrap thead th{background:var(--jz-navy);color:#fff;font-family:'Syne',sans-serif;font-weight:700;font-size:12px;padding:12px 15px;text-align:left;white-space:nowrap}\n.jeez-pl .jz-table-wrap thead th:first-child{border-radius:9px 0 0 0}\n.jeez-pl .jz-table-wrap thead th:last-child{border-radius:0 9px 0 0}\n.jeez-pl .jz-table-wrap tbody td{padding:10px 15px;border-bottom:1px solid var(--jz-border);vertical-align:top;color:var(--jz-text)}\n.jeez-pl .jz-table-wrap tbody tr:nth-child(even){background:var(--jz-bg)}\n.jeez-pl .jz-table-wrap tbody tr:hover{background:var(--jz-teal-xlight)}\n.jeez-pl .jz-table-wrap tbody tr:last-child td{border-bottom:none}\n.jeez-pl .jz-steps{display:flex;flex-direction:column;gap:13px;margin:20px 0}\n.jeez-pl .jz-step{display:flex;gap:16px;align-items:flex-start}\n.jeez-pl .jz-step-num{flex-shrink:0;width:34px;height:34px;background:var(--jz-teal);color:#fff;border-radius:50%;display:flex;align-items:center;justify-content:center;font-family:'Syne',sans-serif;font-weight:800;font-size:13px;margin-top:3px}\n.jeez-pl .jz-step-body{flex:1}\n.jeez-pl .jz-step-body h4{margin:0 0 4px}\n.jeez-pl .jz-step-body p{margin:0;font-size:14px;color:var(--jz-text)}\n.jeez-pl .jz-grid-2{display:grid;grid-template-columns:1fr 1fr;gap:14px;margin:20px 0}\n.jeez-pl .jz-card{border:1px solid var(--jz-border);border-top:3px solid var(--jz-teal);border-radius:var(--jz-radius);padding:20px;background:var(--jz-white)}\n.jeez-pl .jz-card h4{margin:0 0 8px;font-size:.92rem;color:var(--jz-navy)}\n.jeez-pl .jz-card p{margin:0;font-size:13.5px;color:var(--jz-muted);line-height:1.6}\n.jeez-pl .jz-more{display:inline-flex;align-items:center;gap:8px;background:var(--jz-teal-xlight);border:1px solid rgba(13,148,136,.22);border-radius:8px;padding:9px 17px;font-size:13px;font-weight:600;color:var(--jz-teal-dark);text-decoration:none;margin-top:12px;transition:background .15s}\n.jeez-pl .jz-more:hover{background:rgba(13,148,136,.14);color:var(--jz-teal-dark);text-decoration:none}\n.jeez-pl .jz-more-arrow{font-size:14px;flex-shrink:0}\n.jeez-pl .jz-cta-box{background:linear-gradient(140deg,#0B1D3A 0%,#0A3D62 100%);border-radius:16px;padding:44px 48px;text-align:center;margin:50px 0;position:relative;overflow:hidden}\n.jeez-pl .jz-cta-box::before{content:'';position:absolute;left:-70px;bottom:-70px;width:230px;height:230px;border-radius:50%;background:radial-gradient(circle,rgba(13,148,136,.16) 0%,transparent 70%)}\n.jeez-pl .jz-cta-box h3{font-family:'Syne',sans-serif;color:#fff;font-size:1.4rem;font-weight:800;margin:0 0 10px;position:relative}\n.jeez-pl .jz-cta-box p{color:rgba(255,255,255,.74);max-width:520px;margin:0 auto 26px;font-size:14.5px;position:relative}\n.jeez-pl .jz-btn{display:inline-block;background:var(--jz-teal);color:#fff;font-size:14.5px;font-weight:700;padding:13px 36px;border-radius:8px;text-decoration:none;letter-spacing:.02em;position:relative;transition:background .15s,transform .1s}\n.jeez-pl .jz-btn:hover{background:var(--jz-teal-dark);color:#fff;text-decoration:none;transform:translateY(-2px)}\n.jeez-pl .jz-faq-list{margin-top:18px}\n.jeez-pl .jz-faq-item{border:1px solid var(--jz-border);border-radius:var(--jz-radius);margin-bottom:12px;overflow:hidden}\n.jeez-pl .jz-faq-q{background:var(--jz-bg);padding:15px 20px;font-weight:600;font-size:14.5px;color:var(--jz-navy);border-left:4px solid var(--jz-teal);line-height:1.4}\n.jeez-pl .jz-faq-a{padding:14px 20px 16px;font-size:14px;color:var(--jz-text);line-height:1.74;border-top:1px solid var(--jz-border)}\n@media(max-width:680px){.jeez-pl .jz-hero{padding:28px 22px}.jeez-pl .jz-toc ol{columns:1}.jeez-pl .jz-grid-2{grid-template-columns:1fr}.jeez-pl .jz-cta-box{padding:32px 22px}.jeez-pl h2{font-size:1.3rem}}\n<\/style>\n\n<div class=\"jeez-pl\">\n\n<a class=\"jz-back-link\" href=\"https:\/\/jeez-semicon.com\/ja\/blog\/Planarization-in-Semiconductor-Manufacturing-Complete-Guide\/\" target=\"_blank\" rel=\"noopener noreferrer\">\u2190 Back to Complete Planarization Guide<\/a>\n\n<div class=\"jz-hero\">\n  <span class=\"jz-hero-eyebrow\">CMP Process Engineering<\/span>\n  <p class=\"jz-hero-lead\">Chemical Mechanical Planarization combines chemical reactivity and mechanical abrasion to remove material from wafer surfaces and achieve global planarization. This guide provides a thorough technical breakdown of every CMP process step \u2014 from pre-measurement through post-CMP cleaning \u2014 along with equipment anatomy, process variables, endpoint detection methods, and common defect modes.<\/p>\n  <div class=\"jz-hero-meta\">\n    <span>Updated: <strong>June 2026<\/strong><\/span>\n    <span class=\"jz-pipe\">|<\/span>\n    <span>By <strong>JEEZ Technical Team<\/strong><\/span>\n  <\/div>\n<\/div>\n\n<nav class=\"jz-toc\" aria-label=\"\u76ee\u6b21\">\n  <span class=\"jz-toc-label\">\u76ee\u6b21<\/span>\n  <ol>\n    <li><a href=\"#what-makes-cmp-unique\">What Makes CMP Unique<\/a><\/li>\n    <li><a href=\"#preston-equation\">Preston&#8217;s Equation: The Governing Physics<\/a><\/li>\n    <li><a href=\"#equipment\">CMP Equipment Anatomy<\/a><\/li>\n    <li><a href=\"#process-steps\">The CMP Process: Step-by-Step<\/a><\/li>\n    <li><a href=\"#process-variables\">Key Process Variables and Their Effects<\/a><\/li>\n    <li><a href=\"#endpoint-detection\">Endpoint Detection Methods<\/a><\/li>\n    <li><a href=\"#uniformity-control\">Within-Wafer Uniformity Control<\/a><\/li>\n    <li><a href=\"#defects\">Common CMP Defects and Root Causes<\/a><\/li>\n    <li><a href=\"#faq\">\u3088\u304f\u3042\u308b\u8cea\u554f<\/a><\/li>\n  <\/ol>\n<\/nav>\n\n\n<section id=\"what-makes-cmp-unique\">\n  <h2><span class=\"jz-sn\">01<\/span>What Makes CMP Unique Among Planarization Techniques<\/h2>\n  <p>Chemical Mechanical Planarization occupies a category of its own among semiconductor process techniques because it achieves two goals simultaneously that no other process can accomplish together: it removes material at a high, controllable rate (typically 100\u2013600 nm\/min depending on film and recipe), and it produces a globally planar surface whose uniformity spans the full 300 mm wafer diameter. This global planarization capability \u2014 uniquely provided by CMP among all production-ready techniques \u2014 is what makes it indispensable for every advanced-node IC manufacturing flow.<\/p>\n  <p>The technique exploits two synergistic mechanisms that operate simultaneously at the polishing interface:<\/p>\n  <ul>\n    <li><strong>Chemical action:<\/strong> The slurry chemistry reacts with the surface of the film being removed, forming a chemically modified surface layer that is softer, more reactive, or more easily dissolved than the underlying bulk material. For oxide CMP, alkaline silica slurry (pH 10\u201311) breaks surface Si\u2013O\u2013Si bonds. For copper CMP, H\u2082O\u2082 oxidizes Cu to Cu\u2082O. For tungsten CMP, KIO\u2083 or H\u2082O\u2082 forms WO\u2083. This surface modification is what makes CMP dramatically faster than purely mechanical abrasion.<\/li>\n    <li><strong>Mechanical action:<\/strong> Nano-scale abrasive particles (20\u2013200 nm) in the slurry are continuously renewed at the wafer\u2013pad interface by pad rotation and groove geometry. They mechanically remove the chemically modified surface layer, exposing fresh material for the next chemical reaction cycle. Neither the chemical nor the mechanical action alone is sufficient \u2014 together they achieve material removal rates 10\u2013100\u00d7 faster than either mechanism independently.<\/li>\n  <\/ul>\n\n  <div class=\"jz-callout\">\n    <span class=\"jz-callout-tag\">Why synergy matters<\/span>\n    <p>Colloidal silica particles alone \u2014 pressed against SiO\u2082 at CMP pressures \u2014 remove oxide at &lt;5 nm\/min. Alkaline chemistry alone dissolves SiO\u2082 at &lt;2 nm\/min at room temperature. Together in a CMP slurry, they achieve oxide removal rates of 200\u2013500 nm\/min \u2014 demonstrating the multiplicative effect of the chemo-mechanical mechanism.<\/p>\n  <\/div>\n<\/section>\n\n\n<section id=\"preston-equation\">\n  <h2><span class=\"jz-sn\">02<\/span>Preston&#8217;s Equation: The Governing Physics<\/h2>\n  <p>The quantitative relationship governing CMP material removal was first described by Frank Preston in 1927, in the context of optical glass polishing. Preston&#8217;s equation remains the foundational model for CMP process development and equipment design today:<\/p>\n\n  <div class=\"jz-callout blue\">\n    <span class=\"jz-callout-tag\">Preston&#8217;s Equation<\/span>\n    <p style=\"font-size:1.1rem;font-weight:600;color:#0B1D3A;margin:0 0 8px\"><strong>MRR = K<sub>p<\/sub> \u00d7 P \u00d7 V<\/strong><\/p>\n    <p><strong>MRR<\/strong> \u2014 Material Removal Rate (nm\/min or \u00c5\/min)<br>\n    <strong>K<sub>p<\/sub><\/strong> \u2014 Preston coefficient: a material- and slurry-specific constant that captures all chemical, surface energy, and abrasive interaction effects<br>\n    <strong>P<\/strong> \u2014 Contact pressure between the pad and wafer surface (psi or kPa)<br>\n    <strong>V<\/strong> \u2014 Relative velocity between the wafer and pad surfaces (m\/s)<\/p>\n  <\/div>\n\n  <p>The physical implication of Preston&#8217;s equation is profound for planarization: at any point on the wafer, the removal rate is proportional to the local contact pressure. A surface feature that protrudes above the mean plane contacts the polishing pad with higher pressure than a recessed area. Higher pressure \u2192 higher MRR \u2192 the protrusion is removed faster \u2192 the surface converges toward planarity. This self-leveling behavior is the fundamental mechanism that makes CMP uniquely capable of global planarization.<\/p>\n\n  <h3>Limitations and Extensions of Preston&#8217;s Model<\/h3>\n  <p>While Preston&#8217;s equation accurately captures the first-order behavior of CMP, real processes exhibit deviations that advanced models address:<\/p>\n  <ul>\n    <li><strong>Pattern density dependence:<\/strong> The local contact pressure is influenced by the fraction of the pad surface that is in contact with material vs. exposed trenches (the &#8220;pattern density&#8221;). The Preston-Noh-Philipossian model extends Preston to account for this effect.<\/li>\n    <li><strong>Slurry transport limitations:<\/strong> At high pad speeds or low slurry flow rates, fresh slurry may not be efficiently replenished at the wafer center, causing center-edge removal rate asymmetry that deviates from pure Preston behavior.<\/li>\n    <li><strong>Pad viscoelastic effects:<\/strong> Real polyurethane pads are viscoelastic \u2014 their compliance changes with polishing time, temperature, and conditioning history. This introduces time-dependent changes in the effective Preston coefficient during a polishing run.<\/li>\n  <\/ul>\n<\/section>\n\n\n<section id=\"equipment\">\n  <h2><span class=\"jz-sn\">03<\/span>CMP Equipment Anatomy<\/h2>\n  <p>A production CMP system integrates multiple precision-engineered subsystems. Understanding each component&#8217;s role is essential for diagnosing process performance and optimizing recipes.<\/p>\n\n  <div class=\"jz-grid-2\">\n    <div class=\"jz-card\">\n      <h4>Rotary Platen<\/h4>\n      <p>A large (600\u2013700 mm diameter) rigid disk \u2014 stainless steel, granite, or composite \u2014 that holds and rotates the polishing pad. The platen drive controls rotational speed (typically 20\u2013150 rpm) and must maintain extremely tight speed stability (\u00b10.1 rpm) to prevent MRR variation. Platen flatness is critical: run-out &gt;5 \u00b5m can introduce systematic within-wafer uniformity errors.<\/p>\n    <\/div>\n    <div class=\"jz-card\">\n      <h4>Carrier Head (Wafer Chuck)<\/h4>\n      <p>Holds the wafer face-down against the rotating pad. Modern carrier heads use a multi-zone pneumatic pressure system with 4\u20137 independently controlled concentric zones across the wafer diameter, allowing the process engineer to apply differential pressure to compensate for radial removal rate non-uniformity. Retaining rings maintain the wafer&#8217;s lateral position while applying adjustable downward force on the pad edge to control edge-exclusion behavior.<\/p>\n    <\/div>\n    <div class=\"jz-card\">\n      <h4>Polishing Pad Assembly<\/h4>\n      <p>Typically a two-layer stack: a hard, microporous polyurethane top layer (IC1000 or equivalent, Shore D ~55\u201365) affixed over a softer compliant sublayer (SUBA or equivalent). The pad is affixed to the platen via pressure-sensitive adhesive. Groove patterns machined into the pad surface (concentric, radial, X-Y, or spiral) control slurry distribution and prevent hydrodynamic lift-off at high rotation speeds.<\/p>\n    <\/div>\n    <div class=\"jz-card\">\n      <h4>Slurry Delivery System<\/h4>\n      <p>Dispenses slurry at controlled temperature (typically 20\u201325\u00b0C \u00b1 0.5\u00b0C), flow rate (100\u2013300 mL\/min), and, in some systems, point-of-use mixing ratio (for two-part slurries where oxidizer is added just before dispense). In-line particle size monitoring, flow controllers, and point-of-use filtration (0.2\u20131 \u00b5m) are standard in high-volume manufacturing to detect agglomeration events before they reach the wafer.<\/p>\n    <\/div>\n    <div class=\"jz-card\">\n      <h4>Conditioning System<\/h4>\n      <p>A rotating arm holds a diamond conditioning disk (CVD diamond crystals embedded in a metal matrix, 4\u20136 inch diameter) that is pressed against the rotating pad surface. The conditioning disk abrading action continuously removes the glazed, polishing-debris-filled top layer of the pad, exposing fresh pore structure and surface asperities. Conditioning sweep rate, disk force (1\u20138 lbs), and conditioning-to-wafer-polishing ratio (conditioning duty cycle) are key process parameters.<\/p>\n    <\/div>\n    <div class=\"jz-card\">\n      <h4>Endpoint Detection Module<\/h4>\n      <p>Integrated optical windows in the platen allow in-situ reflectometry or interferometry through the pad to the wafer surface. Motor current sensors on the platen and carrier head drives respond to friction changes at the wafer\u2013pad interface. Eddy current sensors (for metal films) detect changes in the electromagnetic properties of the film as thickness decreases toward the target.<\/p>\n    <\/div>\n  <\/div>\n<\/section>\n\n\n<section id=\"process-steps\">\n  <h2><span class=\"jz-sn\">04<\/span>The CMP Process: Step-by-Step<\/h2>\n  <p>A complete CMP process for a single wafer involves the following sequential steps, each contributing critically to the final planarization outcome:<\/p>\n\n  <div class=\"jz-steps\">\n    <div class=\"jz-step\">\n      <div class=\"jz-step-num\">1<\/div>\n      <div class=\"jz-step-body\">\n        <h4>Pre-CMP Incoming Measurement<\/h4>\n        <p>Before the wafer enters the CMP tool, its incoming film thickness profile is measured across a defined grid of points (typically 49\u2013121 points on a 300 mm wafer) by an in-line reflectometry or ellipsometry metrology tool. This data determines the starting thickness distribution, calculates the required removal depth to reach the target post-CMP thickness, and adjusts the polishing time or pressure profile (via run-to-run control) to compensate for process drift from previous lots.<\/p>\n      <\/div>\n    <\/div>\n    <div class=\"jz-step\">\n      <div class=\"jz-step-num\">2<\/div>\n      <div class=\"jz-step-body\">\n        <h4>Pad Break-In and Conditioning<\/h4>\n        <p>A new polishing pad must be &#8220;broken in&#8221; \u2014 conditioned for 20\u201360 minutes before production use \u2014 to stabilize its surface texture and achieve consistent material removal rates. A diamond conditioning disk abrades the pad surface, creating a reproducible population of pad asperities (micro-scale surface protrusions 1\u201310 \u00b5m high) that determine the pad&#8217;s MRR delivery. In-situ conditioning continues during production polishing to maintain pad state. Ex-situ conditioning is performed between wafers to reset the pad surface between lots.<\/p>\n      <\/div>\n    <\/div>\n    <div class=\"jz-step\">\n      <div class=\"jz-step-num\">3<\/div>\n      <div class=\"jz-step-body\">\n        <h4>Slurry Pre-Wetting and Stabilization<\/h4>\n        <p>The pad surface is pre-wetted with slurry or DIW (deionized water) before the wafer contacts the pad. This ensures the pad pores are filled with slurry before polishing begins, avoiding a dry-contact period at wafer-down that can cause excessive friction, wafer slippage, or initial over-polishing. Pre-wetting time (typically 10\u201330 seconds) and slurry flow rate during pre-wetting are recipe-controlled parameters.<\/p>\n      <\/div>\n    <\/div>\n    <div class=\"jz-step\">\n      <div class=\"jz-step-num\">4<\/div>\n      <div class=\"jz-step-body\">\n        <h4>Main Polishing (Bulk Removal)<\/h4>\n        <p>The carrier head lowers the wafer onto the rotating pad. Down-force (1\u20136 psi, independently adjustable per zone on multi-zone heads), platen rotational speed (50\u2013120 rpm), carrier rotational speed (30\u2013100 rpm, counter-rotating or co-rotating relative to platen), carrier sweep oscillation amplitude and frequency, and slurry flow rate are all simultaneously controlled to the target recipe values. The Preston-governed removal begins immediately. Duration is set by the run-to-run control system&#8217;s calculation from the incoming thickness measurement.<\/p>\n      <\/div>\n    <\/div>\n    <div class=\"jz-step\">\n      <div class=\"jz-step-num\">5<\/div>\n      <div class=\"jz-step-body\">\n        <h4>Chemical Reaction at the Polishing Interface<\/h4>\n        <p>Throughout polishing, the slurry chemistry reacts with the wafer surface in a continuously cycling process: chemical species in the slurry modify the surface of the film (forming a softer or more soluble surface compound), abrasive particles mechanically remove the modified surface layer, fresh unmodified material is exposed to further chemical attack, and the cycle repeats. The rate of this cycle \u2014 and therefore the MRR \u2014 is governed by both the slurry chemistry and the mechanical parameters (P \u00d7 V in Preston&#8217;s equation). The contact time is typically milliseconds per asperity contact event, but the continuous rotation ensures thousands of such contact events per second per unit area.<\/p>\n      <\/div>\n    <\/div>\n    <div class=\"jz-step\">\n      <div class=\"jz-step-num\">6<\/div>\n      <div class=\"jz-step-body\">\n        <h4>Endpoint Detection and Polish Stop<\/h4>\n        <p>The CMP tool monitors multiple in-situ signals throughout polishing to detect when the target removal depth has been reached. Optical EPD generates a time-domain signal (reflectance or interference fringe pattern) that changes characteristically as the film thins to the stop layer. Motor current EPD detects the friction change as a harder underlying layer (e.g., Si\u2083N\u2084 in STI CMP) is reached. When the endpoint signal matches the programmed threshold, the system triggers a timed over-polish (typically 5\u201315% of the main polish time) and then lifts the wafer off the pad.<\/p>\n      <\/div>\n    <\/div>\n    <div class=\"jz-step\">\n      <div class=\"jz-step-num\">7<\/div>\n      <div class=\"jz-step-body\">\n        <h4>Post-Polish Rinse (at Tool)<\/h4>\n        <p>Immediately after the carrier head lifts from the pad, the wafer is rinsed on the platen with a high-flow DIW stream to displace bulk slurry from the wafer surface. This first rinse removes the majority of slurry particles and prevents them from drying on the wafer surface \u2014 dried slurry is significantly more difficult to remove in post-CMP cleaning and is a major source of particle defects. The rinse continues for 15\u201330 seconds before the wafer is transferred to the post-CMP cleaning section.<\/p>\n      <\/div>\n    <\/div>\n    <div class=\"jz-step\">\n      <div class=\"jz-step-num\">8<\/div>\n      <div class=\"jz-step-body\">\n        <h4>Post-CMP Cleaning (Cleaner Module)<\/h4>\n        <p>The wafer is transferred to a dedicated cleaning module \u2014 on the same CMP tool platform (integrated) or in a separate cleaning tool. PVA brush scrubbing in dilute chemical solution (citric acid, NH\u2084OH, or DIW depending on the film system) removes residual particles and metallic contamination. Megasonic cleaning in SC1 or DIW dislodges particles from recessed surface features. Final DIW rinse and spin-dry prepare the wafer for post-CMP metrology and the next process step. See our <a href=\"https:\/\/jeez-semicon.com\/ja\/blog\/Post-CMP-Cleaning-Planarization-Metrology-Ensuring-Surface-Quality\/\" target=\"_blank\" rel=\"noopener noreferrer\">complete Post-CMP Cleaning guide<\/a> for full details.<\/p>\n      <\/div>\n    <\/div>\n  <\/div>\n<\/section>\n\n\n<section id=\"process-variables\">\n  <h2><span class=\"jz-sn\">05<\/span>Key Process Variables and Their Effects<\/h2>\n  <p>CMP recipe development involves optimizing a multi-parameter space where each variable affects both removal rate and uniformity:<\/p>\n\n  <div class=\"jz-table-wrap\">\n    <table>\n      <thead>\n        <tr><th>Process Variable<\/th><th>\u5178\u578b\u7684\u306a\u7bc4\u56f2<\/th><th>MRR\u3078\u306e\u5f71\u97ff<\/th><th>Effect on Uniformity<\/th><\/tr>\n      <\/thead>\n      <tbody>\n        <tr><td><strong>Down-force (pressure)<\/strong><\/td><td>1\u20136 psi<\/td><td>Direct (linear per Preston)<\/td><td>Higher P \u2192 center-heavy profile; use zone control to correct<\/td><\/tr>\n        <tr><td><strong>\u30d7\u30e9\u30c6\u30f3\u901f\u5ea6<\/strong><\/td><td>30\u2013120 rpm<\/td><td>Direct (V component)<\/td><td>Higher speed \u2192 more uniform slurry refresh; edge effects at extremes<\/td><\/tr>\n        <tr><td><strong>\u30ad\u30e3\u30ea\u30a2\u901f\u5ea6<\/strong><\/td><td>20\u2013100 rpm<\/td><td>Minor independent effect<\/td><td>Counter-rotation improves radial uniformity<\/td><\/tr>\n        <tr><td><strong>Slurry flow rate<\/strong><\/td><td>100\u2013300 mL\/min<\/td><td>Limited above threshold; below threshold MRR drops<\/td><td>Low flow \u2192 center starvation \u2192 center-low uniformity<\/td><\/tr>\n        <tr><td><strong>Slurry temperature<\/strong><\/td><td>18\u201328\u00b0C<\/td><td>+1\u20133%\/\u00b0C for chemical-dominated processes<\/td><td>Temperature gradient across wafer \u2192 MRR variation<\/td><\/tr>\n        <tr><td><strong>Back pressure<\/strong><\/td><td>0\u20133 psi<\/td><td>Reduces effective down-force at wafer center<\/td><td>Used to reduce center-heavy profiles<\/td><\/tr>\n        <tr><td><strong>Conditioning force<\/strong><\/td><td>1\u20138 lbs<\/td><td>Higher \u2192 faster pad wear \u2192 higher initial MRR<\/td><td>Aggressive conditioning may create center-edge pad texture differences<\/td><\/tr>\n      <\/tbody>\n    <\/table>\n  <\/div>\n<\/section>\n\n\n<section id=\"endpoint-detection\">\n  <h2><span class=\"jz-sn\">06<\/span>Endpoint Detection Methods<\/h2>\n  <p>Accurate, repeatable endpoint detection is one of the most technically demanding aspects of CMP process control. The challenge is to stop polishing at exactly the right film thickness \u2014 thin enough to achieve planarization, but without over-polishing into the stop layer or generating excessive dishing. Three primary EPD methods are used in production:<\/p>\n\n  <h3>Optical Endpoint Detection (OED)<\/h3>\n  <p>A laser or broadband light source is directed through a transparent window in the rotating platen and through the polishing pad onto the wafer surface. The reflected optical signal \u2014 either monochromatic interference fringes (at a single wavelength) or a spectroscopic reflectance spectrum (at multiple wavelengths) \u2014 is analyzed in real time. As the film thins, the optical path length changes, causing the interference pattern to cycle. The number of cycles counted provides a direct measurement of film thickness removed. When the cycle count matches the programmed target, or when the spectrum matches the reference for a &#8220;endpoint reached&#8221; condition, polishing stops. OED is standard for dielectric CMP (oxide, STI) and copper CMP.<\/p>\n\n  <h3>Motor Current \/ Friction Endpoint Detection<\/h3>\n  <p>The friction coefficient between the polishing pad and the wafer surface changes when the polishing transitions from one film to another \u2014 for example, from tungsten to TiN barrier to SiO\u2082. Each material has a different coefficient of friction with the pad and slurry combination, producing a characteristic change in the motor torque required to maintain constant rotational speed. The motor current sensors on the platen drive and carrier head drive continuously monitor this torque signature. A friction-based EPD step fires when the current crosses a threshold corresponding to the stop layer being reached. Motor current EPD is particularly effective for STI CMP (oxide \u2192 nitride transition) and tungsten CMP (W \u2192 TiN\/TiW barrier transition).<\/p>\n\n  <h3>Eddy Current Endpoint Detection (for Metal Films)<\/h3>\n  <p>An electromagnetic coil embedded in the platen induces eddy currents in conductive films on the wafer surface. The amplitude and phase of the reflected electromagnetic signal are proportional to the metal film&#8217;s thickness. As the copper or tungsten film thins during polishing, the eddy current signal changes in a predictable, calibrated manner. Eddy current EPD provides a continuous, in-situ thickness measurement during metal CMP with sub-nm precision, enabling highly accurate polishing stop control without relying on friction changes that may be less sharply defined in metal-to-metal stack transitions.<\/p>\n\n  <a class=\"jz-more\" href=\"https:\/\/jeez-semicon.com\/ja\/blog\/Post-CMP-Cleaning-Planarization-Metrology-Ensuring-Surface-Quality\/\" target=\"_blank\" rel=\"noopener noreferrer\">\n    <span>Full metrology guide: Post-CMP Cleaning &amp; Planarization Metrology<\/span>\n    <span class=\"jz-more-arrow\">\u2192<\/span>\n  <\/a>\n<\/section>\n\n\n<section id=\"uniformity-control\">\n  <h2><span class=\"jz-sn\">07<\/span>Within-Wafer Uniformity Control<\/h2>\n  <p>Achieving WIWNU below 1% across a 300 mm wafer requires active, multi-parameter process control. The primary tool for uniformity correction is the <strong>multi-zone carrier head<\/strong>: by independently adjusting the pneumatic pressure in each of the 4\u20137 concentric zones (center, inner-middle, middle, outer-middle, edge, retaining ring zone), the process engineer can directly shape the radial removal rate profile across the wafer. A center-heavy removal profile is corrected by reducing center zone pressure; an edge-heavy profile is corrected by reducing edge zone pressure. Modern CMP tools perform automatic zone pressure adjustment based on incoming film thickness maps, implementing closed-loop run-to-run control that maintains WIWNU within specification as consumable aging occurs.<\/p>\n  <p>Beyond carrier head zone pressure, uniformity is managed by: (1) slurry temperature uniformity (delivered via temperature-controlled supply lines); (2) platen flatness maintenance (periodic platen re-lapping); (3) pad conditioning uniformity (conditioning sweep profile optimization to avoid center-edge differences in pad texture); and (4) slurry flow rate uniformity (multiple dispense nozzles for large pad diameters).<\/p>\n<\/section>\n\n\n<section id=\"defects\">\n  <h2><span class=\"jz-sn\">08<\/span>Common CMP Defects and Root Causes<\/h2>\n\n  <div class=\"jz-grid-2\">\n    <div class=\"jz-card\">\n      <h4>\u8868\u9762\u306e\u50b7<\/h4>\n      <p>Large particles (from slurry agglomeration, pad debris, or contamination) dragged across the wafer surface at the CMP interface. Scratches are the most yield-damaging CMP defect, as they can extend across multiple die and sever multiple metal lines or vias simultaneously. Root causes: slurry agglomeration (inadequate storage or temperature excursions), point-of-use filtration failure, and pad contamination from previous lots.<\/p>\n    <\/div>\n    <div class=\"jz-card\">\n      <h4>\u30c7\u30a3\u30c3\u30b7\u30f3\u30b0<\/h4>\n      <p>Over-polishing of metal lines or features relative to the surrounding dielectric in damascene CMP. Dishing appears as a concave depression in wide copper or tungsten features and is caused by the continued polishing of the soft metal after the harder surrounding dielectric reaches the endpoint. Controlled by limiting over-polish time, optimizing slurry chemistry (BTA concentration for copper), and reducing down-force during the final clearing step.<\/p>\n    <\/div>\n    <div class=\"jz-card\">\n      <h4>\u6d78\u98df<\/h4>\n      <p>Pattern-density-dependent thinning of the dielectric in dense metal arrays \u2014 the cumulative result of the slurry removing dielectric material from between closely spaced metal lines more rapidly than in isolated regions. Erosion creates a &#8220;global&#8221; topographic variation at the pattern scale. Managed through CMP recipe optimization, the use of dummy fill features (added in the IC layout to equalize pattern density), and slurry selectivity tuning.<\/p>\n    <\/div>\n    <div class=\"jz-card\">\n      <h4>\u30c7\u30e9\u30df\u30cd\u30fc\u30b7\u30e7\u30f3<\/h4>\n      <p>Separation of a thin film from the layer below it during CMP, driven by shear stress at the wafer\u2013pad interface. Particularly problematic for ultra-low-k (ULK) porous dielectric films (k &lt; 2.3), which have very low cohesive and adhesive strength. Prevented by using reduced down-force, soft (compliant) pad stacks, and optimized slurry pH for ULK-compatible surface chemistry.<\/p>\n    <\/div>\n    <div class=\"jz-card\">\n      <h4>Metal Corrosion<\/h4>\n      <p>Chemical attack of exposed copper, cobalt, or ruthenium surfaces by slurry chemical agents during or after polishing, producing pitting, oxide growth, or galvanic corrosion where dissimilar metals are exposed simultaneously. Controlled by matching oxidizer type and concentration to the specific metal stack and by minimizing wafer exposure time between CMP polishing and post-CMP cleaning.<\/p>\n    <\/div>\n    <div class=\"jz-card\">\n      <h4>Residues<\/h4>\n      <p>Incompletely cleared barrier metal (TaN, TiN) or dielectric material remaining on the wafer surface after polishing \u2014 a &#8220;clearing failure.&#8221; Causes electrical shorts between adjacent copper lines if barrier metal bridges the dielectric between lines. Addressed by extending the clearing over-polish time, increasing barrier removal rate (slurry composition), or reducing the dielectric pattern density to lower the clearing endpoint variability.<\/p>\n    <\/div>\n  <\/div>\n\n  <a class=\"jz-more\" href=\"https:\/\/jeez-semicon.com\/ja\/blog\/CMP-Slurry-for-Semiconductor-Planarization-Chemistry-Types-Selection\/\" target=\"_blank\" rel=\"noopener noreferrer\">\n    <span>Related: CMP Slurry for Semiconductor Planarization \u2014 Chemistry, Types &amp; Selection<\/span>\n    <span class=\"jz-more-arrow\">\u2192<\/span>\n  <\/a>\n<\/section>\n\n\n<div class=\"jz-cta-box\">\n  <h3>Optimize Your CMP Process with JEEZ Consumables<\/h3>\n  <p>JEEZ manufactures CMP polishing slurries, polishing pads, and absorption films engineered for consistent, high-uniformity planarization across oxide, STI, tungsten, and copper CMP applications. Contact our technical team to discuss your process requirements.<\/p>\n  <a class=\"jz-btn\" href=\"https:\/\/jeez-semicon.com\/ja\/contact\/\" target=\"_blank\" rel=\"noopener noreferrer\">Contact JEEZ \u2192<\/a>\n<\/div>\n\n\n<section id=\"faq\">\n  <h2><span class=\"jz-sn\">\u3088\u304f\u3042\u308b\u3054\u8cea\u554f<\/span>\u3088\u304f\u3042\u308b\u8cea\u554f<\/h2>\n  <div class=\"jz-faq-list\">\n    <div class=\"jz-faq-item\">\n      <div class=\"jz-faq-q\">What are the basic steps of the CMP process?<\/div>\n      <div class=\"jz-faq-a\">The CMP process follows eight key steps: (1) pre-CMP incoming film thickness measurement; (2) pad break-in and conditioning; (3) slurry pre-wetting; (4) main polishing with controlled pressure and velocity; (5) chemical reaction at the polishing interface; (6) endpoint detection and polish stop; (7) post-polish rinse on the tool; and (8) post-CMP cleaning in a dedicated cleaning module. Each step contributes to the final planarization quality and must be optimized as part of the overall recipe development process.<\/div>\n    <\/div>\n    <div class=\"jz-faq-item\">\n      <div class=\"jz-faq-q\">What is Preston&#8217;s equation and why does it matter for CMP?<\/div>\n      <div class=\"jz-faq-a\">Preston&#8217;s equation states MRR = Kp \u00d7 P \u00d7 V, where MRR is the material removal rate, Kp is the Preston coefficient (material- and slurry-specific), P is the contact pressure, and V is the relative velocity between wafer and pad. It matters for CMP because it explains the self-leveling behavior that produces global planarization: elevated surface features experience higher contact pressure (P), which increases their local MRR, causing them to be removed faster than recessed areas until the surface converges toward planarity.<\/div>\n    <\/div>\n    <div class=\"jz-faq-item\">\n      <div class=\"jz-faq-q\">How does endpoint detection work in CMP?<\/div>\n      <div class=\"jz-faq-a\">CMP endpoint detection uses three principal methods: (1) Optical EPD \u2014 laser light directed through the platen and pad onto the wafer surface; interference fringe changes track film thickness in real time; (2) Motor current EPD \u2014 friction changes as the polishing transitions from one film to another are detected as changes in platen or carrier motor torque; and (3) Eddy current EPD \u2014 for conductive films, an electromagnetic coil measures metal film thickness by the eddy current response. All three methods can stop polishing automatically when the target film thickness or stop layer is reached.<\/div>\n    <\/div>\n    <div class=\"jz-faq-item\">\n      <div class=\"jz-faq-q\">What causes scratches in CMP and how are they prevented?<\/div>\n      <div class=\"jz-faq-a\">CMP scratches are caused by large particles (slurry agglomerates, pad debris, or contamination) dragged across the wafer surface. Prevention strategies include: strict slurry storage temperature control (to prevent agglomeration); point-of-use filtration (0.2\u20131 \u00b5m in-line filters); pad cleaning between wafers; slurry expiry date management; and regular inspection of slurry supply lines for contamination. Post-CMP optical inspection with bright-field and dark-field imaging is used to detect and monitor scratch defect density as a process health indicator.<\/div>\n    <\/div>\n    <div class=\"jz-faq-item\">\n      <div class=\"jz-faq-q\">What is dishing in copper CMP and how is it controlled?<\/div>\n      <div class=\"jz-faq-a\">Dishing in copper CMP refers to the concave depression that forms in wide copper features when the soft copper continues to be polished after the surrounding harder dielectric reaches the endpoint level. It is controlled by: limiting the over-polish time after barrier clearance; using slurry chemistry with benzotriazole (BTA) as a corrosion inhibitor that forms a passivation layer on exposed copper, reducing its MRR relative to the dielectric; reducing down-force during the final clearing step; and using fixed-abrasive pad systems for low-dishing applications such as hybrid bonding preparation.<\/div>\n    <\/div>\n  <\/div>\n<\/section>\n\n<\/div>\n\n<script type=\"application\/ld+json\">\n{\n  \"@context\": \"https:\/\/schema.org\",\n  \"@type\": \"FAQPage\",\n  \"mainEntity\": [\n    {\"@type\":\"Question\",\"name\":\"What are the basic steps of the CMP process?\",\"acceptedAnswer\":{\"@type\":\"Answer\",\"text\":\"The CMP process follows eight key steps: pre-CMP incoming measurement, pad break-in and conditioning, slurry pre-wetting, main polishing, chemical reaction at the interface, endpoint detection and stop, post-polish rinse, and post-CMP cleaning. Each step contributes to the final planarization quality.\"}},\n    {\"@type\":\"Question\",\"name\":\"What is Preston's equation and why does it matter for CMP?\",\"acceptedAnswer\":{\"@type\":\"Answer\",\"text\":\"Preston's equation: MRR = Kp \u00d7 P \u00d7 V. It matters because elevated surface features experience higher contact pressure (P), increasing their removal rate, causing them to be polished away faster than recessed areas \u2014 the self-leveling behavior that produces global planarization.\"}},\n    {\"@type\":\"Question\",\"name\":\"How does endpoint detection work in CMP?\",\"acceptedAnswer\":{\"@type\":\"Answer\",\"text\":\"Three methods: (1) Optical EPD \u2014 laser interference fringe changes track film thickness in real time; (2) Motor current EPD \u2014 friction changes between films detected as torque changes; (3) Eddy current EPD \u2014 electromagnetic coil measures metal film thickness for conductive film CMP.\"}},\n    {\"@type\":\"Question\",\"name\":\"What causes scratches in CMP and how are they prevented?\",\"acceptedAnswer\":{\"@type\":\"Answer\",\"text\":\"Scratches are caused by large particles (slurry agglomerates, pad debris) dragged across the wafer. Prevention: strict slurry storage temperature control, point-of-use filtration, pad cleaning between wafers, and slurry expiry management.\"}}\n  ]\n}\n<\/script>","protected":false},"excerpt":{"rendered":"<p>\u2190 Back to Complete Planarization Guide CMP Process Engineering Chemical Mechanical Planarization combines chemical reactivity and mechanical abrasion to remove material from wafer surfaces and achieve global planarization. This guide  &#8230;<\/p>","protected":false},"author":1,"featured_media":2376,"comment_status":"closed","ping_status":"closed","sticky":false,"template":"","format":"standard","meta":{"_acf_changed":false,"footnotes":""},"categories":[9,59],"tags":[],"class_list":["post-2374","post","type-post","status-publish","format-standard","has-post-thumbnail","hentry","category-blog","category-industry"],"acf":[],"_links":{"self":[{"href":"https:\/\/jeez-semicon.com\/ja\/wp-json\/wp\/v2\/posts\/2374","targetHints":{"allow":["GET"]}}],"collection":[{"href":"https:\/\/jeez-semicon.com\/ja\/wp-json\/wp\/v2\/posts"}],"about":[{"href":"https:\/\/jeez-semicon.com\/ja\/wp-json\/wp\/v2\/types\/post"}],"author":[{"embeddable":true,"href":"https:\/\/jeez-semicon.com\/ja\/wp-json\/wp\/v2\/users\/1"}],"replies":[{"embeddable":true,"href":"https:\/\/jeez-semicon.com\/ja\/wp-json\/wp\/v2\/comments?post=2374"}],"version-history":[{"count":2,"href":"https:\/\/jeez-semicon.com\/ja\/wp-json\/wp\/v2\/posts\/2374\/revisions"}],"predecessor-version":[{"id":2377,"href":"https:\/\/jeez-semicon.com\/ja\/wp-json\/wp\/v2\/posts\/2374\/revisions\/2377"}],"wp:featuredmedia":[{"embeddable":true,"href":"https:\/\/jeez-semicon.com\/ja\/wp-json\/wp\/v2\/media\/2376"}],"wp:attachment":[{"href":"https:\/\/jeez-semicon.com\/ja\/wp-json\/wp\/v2\/media?parent=2374"}],"wp:term":[{"taxonomy":"category","embeddable":true,"href":"https:\/\/jeez-semicon.com\/ja\/wp-json\/wp\/v2\/categories?post=2374"},{"taxonomy":"post_tag","embeddable":true,"href":"https:\/\/jeez-semicon.com\/ja\/wp-json\/wp\/v2\/tags?post=2374"}],"curies":[{"name":"wp","href":"https:\/\/api.w.org\/{rel}","templated":true}]}}